作者： The wear resistance test standard for solid wood products is that the weight of the paint film is less than 0.15g per 100 rotations (and the paint film is not worn through). The measured value of our floor is less than 0.02g, which is far higher than the national stipulated value.
Formaldehyde emission. The formaldehyde emission of floor reached 0.1 mg/L, which was far below the E0 standard of 0.5 mg/L.
Static bending strength. The actual floor test result is 62.5 MPa, which is more than twice as high as the national standard of 30 MPa.
Adhesion of paint film. The national standard stipulates that a small amount of intermittent peeling is allowed after the use of marking paint, and no peeling is allowed in the actual floor testing.
Formaldehyde emission. The formaldehyde emission of floor reached 0.1 mg/L, which was far below the E0 standard of 0.5 mg/L.
Static bending strength. The actual floor test result is 62.5 MPa, which is more than twice as high as the national standard of 30 MPa.
Adhesion of paint film. The national standard stipulates that a small amount of intermittent peeling is allowed after the use of marking paint, and no peeling is allowed in the actual floor testing.